PRODUCT
: |
BODYLITE
230 |
|
PRODUCT
CODE: |
230.07.000.04 |
SPECIFICATION
CODE: |
QASS026A |
DATE |
30.03.2003 |
|
|
|
System
Description |
Light
polyester filler. |
|
Shade |
Light
grey |
|
Application
Field(s) |
For the filling of cavities and rotten areas of metallic and wooden
surfaces. |
|
PROPERTY |
UNIT |
DRY FILM THICKNESS [μm] |
MEASUREMENT AFTER |
VALUE |
STANDARD |
|
Specific
gravity |
g/cm3 |
|
|
1.20±0.10 |
DIN
53 217 |
|
Maximum
particle size |
μm |
|
|
<50 |
DIN
EN 21 524 |
|
Total
solids (w/w) |
% |
|
|
84
±
3 |
DIN
EN ISO 3251 |
|
Flash
Point |
ο
C |
|
|
31 |
DIN
EN 456 |
|
Cup6
Viscosity
(20ο C±0.5) |
Sec |
|
|
|
DIN
53 211 |
|
EUROPHYSICS
Viscosity (25οC±0.5) |
Pas |
|
|
|
|
|
Dry-to-the-touch
(23ο C±0.5) |
min |
150 |
|
10-15 |
|
|
Full
hardness
(23ο C±0.5) |
min |
150 |
|
20-30 |
|
|
Full
hardness
( 60ο C±2 ) |
min |
|
|
|
|
|
Full
hardness IR |
min |
150 |
|
5-8 |
|
|
Full
hardness according to KOENIG |
sec |
|
|
|
DIN
53 157 |
|
Theoretical
Spreading Rate |
m2/Kg |
|
|
|
- |
MECHANICAL PROPERTIES
|
PROPERTY |
UNIT |
DRY FILM THICKNESS [μm] |
MEASUREMENT AFTER |
VALUE |
STANDARD |
|
Elasticity
acc. to ERICHSEN |
mm |
150 |
1
h |
>2 |
DIN
EN ISO 1520 |
|
Elasticity
acc. to MANDREL |
o |
150 |
1
h |
Pass
3 |
DIN
EN ISO 1519 |
|
Impact
Test |
cm |
150 |
1
h |
20 |
|
|
Cross
cut |
GT |
150 |
1
h |
0-1 |
DIN
EN ISO 2409 |
CHEMICAL RESISTANCE
|
PROPERTY |
UNIT |
MEASUREMENT AFTER |
EXPOSURE TIME [hrs] |
RESULT |
|
Salt
Spray Test ASTM B-117-90 |
hours |
|
|
|
|
Q-UV |
hours |
|
|
|
|
Water |
hours |
|
|
|
|
Motor
Oil |
hours |
|
|
|
|
Diesel
Oil |
hours |
|
|
|
|
Unleaded
Gasoline (SUPER) |
minutes |
|
|
|
|
ΝαΟΗ
0.5% |
minutes |
|
|
|
|
Η2SO4
10% |
minutes |
|
|
|
PRETREATMENT AND APPLICATION OF THE MATERIAL
|
Hardener
addition |
Paint
: Hardener = 100:3 w/w |
||
|
Type
of hardener |
Dibenzoylperoxide |
Product
Code |
|
|
Thinner
addition [%] |
|
||
|
Type
of thinner |
|
Product
Code |
|
|
Application
Viscosity Cup6 (sec) |
|
Temperature
(23ο C±0.5) |
|
|
Pot
life [min] |
3-4 |
||
|
Repaintable
after [hours] |
|
||
|
Mode
of Application |
Spatula |
||
|
Spray
Gun Nozzle Diameter [mm] |
|
||
|
Suggested
Dry Film Thickness [μm] |
100-200 |
||
|
Maximum
Storage Time (months) |
24 |
|
Suggested
Storage Temperature [οC] |
+5
to +25 |
A
two component spatula filling compound based on polyester, suitable for metallic
and wooden surfaces. Stir the contents well before use. Add hardener 2-3% v/v
and mix well with putty. You have 4-5 minutes time to apply with the spatula
before it starts hardening.
Dries
quickly, is sanded easily and a sandpaper P80-180 must be used in order to give
a fine, non porous surface.
Flammable.
Use only in well ventilated areas. Do not breathe vapour.
Keep
out of reach of children.