PRODUCT
: |
BODY
225 UNI-FINE |
|
PRODUCT
CODE: |
225.01.0000.1 |
SPECIFICATION
CODE: |
QASS028A |
DATE: |
30.10.2003 |
|
System
Description |
2K
Polyester filler. |
|
Shade |
White. |
|
Application
Field(s) |
For the filling of cavities and rooten areas of galvinized steel,
stainless steel, normal grade metal sheet and aluminium, as well as
plastic bumpers except PE (Polyethylene). |
|
PROPERTY |
UNIT |
DRY FILM THICKNESS [μm] |
MEASUREMENT AFTER |
VALUE |
STANDARD |
|
Specific
gravity |
g/cm3 |
|
|
1.70-1.80 |
DIN
53 217 |
|
Maximum
particle size |
μm |
|
|
<40 |
DIN
EN 21 524 |
|
Total
solids (w/w) |
% |
|
|
82
±
5 |
DIN
EN ISO 3251 |
|
Flash
Point |
ο
C |
|
|
31 |
DIN
EN 456 |
|
Cup
4 Viscosity
(20ο
C±0.5) |
sec |
|
|
|
DIN
53 211 |
|
EUROPHYSICS
Viscosity (25οC±0.5) |
Pa.s |
|
|
|
|
|
Dry-to-the-touch
(23ο
C±0.5) |
min |
150 |
|
10
– 15 |
|
|
Full
hardness
(23ο C±0.5) |
hrs |
150 |
|
20
– 30 |
|
|
Full
hardness
( 60ο C±2 ) |
hrs |
|
|
|
|
|
Fullhardness
IR |
min |
150 |
|
5-8 |
|
|
Full
hardness according to KOENIG |
sec |
|
|
|
DIN
53 157 |
|
Theoretical
Spreading Rate |
m2/kg |
|
|
|
|
MECHANICAL PROPERTIES
|
PROPERTY |
UNIT |
DRY FILM THICKNESS [μm] |
MEASUREMENT AFTER |
VALUE |
STANDARD |
|
Εlasticity
acc. to ERICHSEN |
mm |
150 |
1
h |
>
2 |
DIN
EN ISO 1520 |
|
Bending
test acc. to MANDREL |
o |
150 |
1
h |
Pass
3 |
DIN
EN ISO 1519 |
|
Impact
Test |
cm |
150 |
1
h |
10 |
|
|
Cross
cut |
GT |
150 |
1
h |
0-1 |
DIN
EN ISO 2409 |
|
PROPERTY |
UNIT |
MEASUREMENT AFTER |
EXPOSURE TIME [hours] |
RESULT |
|
Salt
spray test ASTM B-117-90 |
hours |
|
|
|
|
Q-UV |
hours |
|
|
|
|
Water |
hours |
|
|
|
|
Motor
Oil |
hours |
|
|
|
|
Diesel
Oil |
hours |
|
|
|
|
Unleaded
Gasoline (Super) |
minutes |
|
|
|
|
ΝαΟΗ
0.5% |
minutes |
|
|
|
|
Η2SO4
10% |
minutes |
|
|
|
PRETREATMENT AND APPLICATION OF THE MATERIAL
|
Hardener
addition |
Paint
: Hardener = 100 : 3 v/v |
||
|
Τype
of hardener |
Dibenzoylperoxide |
Product
Code |
|
|
Thinner
Addition [%] |
|
||
|
Τype
of thinner |
|
Product
Code |
|
|
Application
Viscosity DIN 53 211 Cup4 [sec] |
|
Temperature
(23ο C±0.5) |
|
|
Pot
life [min] |
4 |
||
|
Repaintable
after [hrs] |
|
||
|
Mode
of Application |
Spatula |
||
|
Spray
Gun Nozzle diameter [mm] |
|
||
|
Suggested
dry film thickness [μm] |
100
– 200 |
||
|
Maximum
Storage Time (months) |
24 |
|
Recommended
Storage Temperature [οC] |
+5
to +25 |
A
two component spatula filling compound based on polyester, suitable for
galvinized steel, stainless steel, normal grade metal sheet and aluminium, as
well as for plastic Bumpers except PE (Polyethylene).
Stir
the contents well before use. Add hardener 2-3% v/v and mix well with putty. You
have 4-5 minutes time to apply with the spatula before it starts hardening.
Dries
quickly, is sanded easily and a sandpaper P150 - 400 must be used in order to
give a fine, non porous surface.
Flammable.
Use only in well ventilated areas. Do not drink/eat, avoid any inhalation of
vapour and skin contact.
Keep
out of reach of children.